Chemical Ranges Carbon Steel.
|
Chemical Composition Limits, percent |
|
AISI
or
SAE |
C |
Mn |
P
Max. |
S
Max. |
|
1005*
1006*
1008
1010 |
.06 max
.08 max
.10 max.
.08/.13 |
.35 max
.25/.40
.30/.50
.30/.60 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1011*
1012
1013*
1015 |
.08/.13
.10/.15
.11/.16
.13/.18 |
.60/.90
.30/.60
.50/.80
.30/.60 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1016
1017
1018
1019 |
.13/.18
.15/.20
.15/.20
.15/.20 |
.60/.90
.30/.60
.60/.90
.70/1.00 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1020
1021
1022
1023 |
.18/.23
.18/.23
.18/.23
.20/.25 |
.30/.60
.60/.90
.70/1.00
.30/.60 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1025
1026
1029
1030 |
.22/.28
.22/.28
.25/.31
.28/.34 |
.30/.60
.60/.90
.60/.90
.60/.90 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1035
1037
1038
1039 |
.32/.38
.32/.38
.35/.42
.37/.44 |
.60/.90
.70/1.00
.60/.90
.70/1.00 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1040
1042
1043
1044 |
.37/.44
.40/.4?
.40/.47
.43/.50 |
.60/.90
.60/.90
.70/1.00
.30/.60 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1045
1046
1049
1050 |
.43/.50
.43/.50
.46/.53
.48/.55 |
.60/.90
.70/1.00
.60/.90
.60/.90 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1053
1055
1059*
1060
1064* |
.48/.55
.50/.60
.55/.65
.55/.65
.60/.70 |
.70/1.00
.60/.90
.50/.80
.60/.90
.50/.80 |
.040
.040
.040
.040
.040 |
.050
.050
.050
.050
.050 |
|
1065*
1069*
1070
1074* |
.60/.70
.65/.75
.65/.75
.70/.80 |
.60/.90
.40/.70
.60/.90
.50/.80 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1075*
1078
1080
1084 |
.70/.80
.72/.85
.75/.88
.80/.93 |
.40/.70
.30/.60
.60/.90
.60/.90 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
|
1085*
1086*
1090
1095 |
.80/.93
.80/.93
.85/.98
.90/1.03 |
.70/1.00
.30/.50
.60/.90
.30/.50 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
* SAE Only
CARBON-MANGANESE STEELS
(Manganese Maximum Over 1.00 Per Cent)
|
Chemical Composition Limits, percent |
|
AISI
or
SAE |
C |
Mn |
P
Max. |
S
Max. |
|
1513
1518*
1522
1524 |
0.10/0.16
0.15/0.21
0.18/0.24
0.19/0.25 |
1.10/1.40
1.10/1.40
1.10/1.40
1.35/1.65 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
|
1525*
1526
1527
1533 |
0.23/0.29
0.22/0.29
0.22/0.29
0.30/0.37 |
0.80/1.10
1.10/1.40
1.20/1.50
1.10/1.40 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
|
1534
1536
1541
1544 |
0.30/0.37
0.30/0.37
0.36/0.44
0.40/0.47 |
1.20/1.50
1.20/1.50
1.35/1.65
0.80/1.10 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
|
1545
1546
1547*
1548 |
0.43/0.50
0.44/0.52
0.43/0.51
0.44/0.52 |
0.80/1.10
1.00/1.30
1.35/1.65
1.10/1.40 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
|
1551
1552
1553
1566 |
0.45/0.56
0.47/0.55
0.48/0.55
0.60/0.71 |
0.85/1.15
1.20/1.50
0.80/1.10
0.85/1.15 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
|
1570
1572
1580
1590 |
0.65/0.75
0.65/0.76
0.75/0.88
0.85/0.98 |
0.80/1.10
1.00/1.30
0.80/1.10
0.80/1.10 |
0.040
0.040
0.040
0.040 |
0.050
0.050
0.050
0.050 |
*SAE only
|
Note 1. Silicon When silicon ranges or limits are required, consult producer for ranges and limits.
Note 2. Copper When copper is required, 0.020 per cent minimum is generally specified.
Note 3. Lead See footnote for lead under Table 2.
|
CARBON "H" GRADES
|
Chemical Composition Limits, percent |
|
Grade
No. |
C |
Mn |
P
Max. |
S
Max. |
Si |
|
1038-H
1045-H
1522-H
1524-H |
.34/.43
.42/.51
.17/.25
.18/.26 |
.50/1.00 .50/1.00
1.00/1.50
1.25/1.75 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
.15/.35
.15/.35
.15/.35
.15/.35 |
|
1526-H
1541-H |
.21/.30
.35/.45 |
1.00/1.50
1.25/1.75 |
.040
.040 |
.050
.050 |
.15/.35
.15/.35 |
CARBON BORON "H" GRADES
(These steels can be expected to contain 0.0005 to 0.003 percent Boron)
|
Chemical Composition Limits, percent |
|
Grade
No. |
C |
Mn |
P
Max. |
S
Max. |
Si |
|
15821H
15B35H
15637H
15B41H |
.17/.24
.31/.39
.30/.39
.35/.45 |
.70/1.20
.70/1.20
1.00/1.50
1.25/1.75 |
.040
.040
.040
.040 |
.050
.050
.050
.050 |
.15/.35
.15/.35
.15/.35
.15/.35 |
|
15B48H
15B62H |
.43/.53
.54/.67 |
1.00/1.50
1.00/1.50 |
.040
.040 |
.050
.050 |
.15/.35
.40/.60 |
Silicon. When silicon is required, the following ranges and limits are commonly used:
RESULFURIZED CARBON STEELS
HEAT CHEMICAL RANGES AND LIMITS
|
Chemical Composition Limits, percent |
|
AISI
or
SAE |
C |
Mn |
P
Max. |
S
Max. |
|
1108*
1109*
1110
1117 |
.08/.13
.08/.13
.08/.13
.14/.20 |
.50/.80
.60/.90
.30/.60
1.00/1.30 |
.040
.040
.040
.040 |
.08/.13
.08/.13
.08/.13
.08/.13 |
|
1118
1119*
1132*
1137 |
.14/.20
.14/.20
.27/.34
.32/.39 |
1.30/1.60
1.00/1.30
1.35/1.65
1.35/1.65 |
.040
.040
.040
.040 |
.08/.13
.24/.33
.08/.13
.08/.13 |
|
1139
1140
1141
1144 |
.35/.43
.37/.44
.37/.45
.40/.48 |
1.35/1.65
.70/1.00
1.35/1.65
1.35/1.65 |
.040
.040
.040
.040 |
.13/.20
.08/.13
.08/.13
.24/.33 |
|
1145*
1146
1152 |
.42/49
.42/49
.48/55 |
.70/1.00
.70/1.00
.70/1.00 |
.040
.040
.040 |
.04/.07
.08/.13
.06/.09 |
*SAE Only
Silicon: When silicon is required, the following ranges and limits are commonly used.
REPHOSPHORIZED AND RESULFURIZED CARBON STEELS
HEAT CHEMICAL RANGES AND LIMITS
|
Chemical Composition Limits, percent |
|
Grade No. |
C
Max. |
Mn |
P |
S |
|
1212
1213
12L14
1215 |
.13
.13
.15
09 |
.70/1.00
.70/1.00
.85/1.15
75/1.05 |
.07/.12
.07/.12
.04/.09
04/09 |
.16/.23
.24/.33
.26/.35
Pb-.15/.35
.26/.35 |
Silicon: It is not common practice to produce these steels to specified limits for silicon.
Lead: When required, lead is specified as an added element to a standard steel and is identified by inserting letter "L" between second and third numerals.
NOTE: The chemical ranges and limits shown are subject to the check analysis tolerance shown in the A.I.S.I. Manual for Alloy, Carbon and HSLA Steels.